Structures published

Total: 20

Au V

Au_1.04V_0.96

Koester, W.Nordskog, H.

Zeitschrift fuer Metallkunde (1960) 51, 501-502

a=3.986Å b=3.986Å c=3.986Å

α=90° β=90° γ=90°

Ag₂Ba

Meixner, J.Koester, W.

Zeitschrift fuer Metallkunde (1965) 45, 695-703

a=4.958Å b=8.063Å c=8.453Å

α=90° β=90° γ=90°

Ag₂Sr

Koester, W.Meixner, J.

Zeitschrift fuer Metallkunde (1965) 56, 695-703

a=4.817Å b=7.71Å c=8.263Å

α=90° β=90° γ=90°

Ag₂Eu

Koester, W.Meixner, J.

Zeitschrift fuer Metallkunde (1965) 56, 695-703

a=4.753Å b=7.488Å c=8.164Å

α=90° β=90° γ=90°

PdV₃

Koester, W.Haehl, W.D.

Zeitschrift fuer Metallkunde (1958) 49, 647-649

a=4.816Å b=4.816Å c=4.816Å

α=90° β=90° γ=90°

InP

Koester, W.Ulrich, W.

Zeitschrift fuer Metallkunde (1958) 49, 365-367

a=5.88Å b=5.88Å c=5.88Å

α=90° β=90° γ=90°

Pd₃V

Koester, W.Gmoehling, W.

Zeitschrift fuer Metallkunde (1960) 51, 385-391

a=3.85Å b=3.85Å c=3.85Å

α=90° β=90° γ=90°

(Ni0.375 Pd0.375 V0.25)

Ni_0.375Pd_0.375V_0.25

Koester, W.Gmoehling, W.

Zeitschrift fuer Metallkunde (1960) 51, 385-391

a=3.75Å b=3.75Å c=3.75Å

α=90° β=90° γ=90°

(Ni3 V)

Ni₃V

Koester, W.Gmoehling, W.

Zeitschrift fuer Metallkunde (1960) 51, 385-391

a=3.56Å b=3.56Å c=3.56Å

α=90° β=90° γ=90°

(Ni1.5 V0.5)

Ni_1.5V_0.5

Koester, W.Gmoehling, W.

Zeitschrift fuer Metallkunde (1960) 51, 385-391

a=2.5Å b=2.5Å c=3.61Å

α=90° β=90° γ=90°

Cd₂Sr

Koester, W.Meixner, J.

Zeitschrift fuer Metallkunde (1965) 56, 695-703

a=5.046Å b=8.008Å c=8.451Å

α=90° β=90° γ=90°

(Co Ir)

CoIr

Koester, W.Horn, E.

Zeitschrift fuer Metallkunde (1952) 43, 444-449

a=3.69Å b=3.69Å c=3.69Å

α=90° β=90° γ=90°

(Co Ir)

CoIr

Koester, W.Horn, E.

Zeitschrift fuer Metallkunde (1952) 43, 444-449

a=2.625Å b=2.625Å c=4.187Å

α=90° β=90° γ=120°

(Co Re)

CoRe

Koester, W.Horn, E.

Zeitschrift fuer Metallkunde (1952) 43, 444-449

a=2.636Å b=2.636Å c=4.265Å

α=90° β=90° γ=120°

(Co Rh)

CoRh

Koester, W.Horn, E.

Zeitschrift fuer Metallkunde (1952) 43, 444-449

a=3.67Å b=3.67Å c=3.67Å

α=90° β=90° γ=90°

(Co Ru)

CoRu

Koester, W.Horn, E.

Zeitschrift fuer Metallkunde (1952) 43, 444-449

a=2.6Å b=2.6Å c=4.165Å

α=90° β=90° γ=120°

(Co0.3 Pd2.7) V

Co_0.3Pd_2.7V

Koester, W.Gmoehling, W.

Zeitschrift fuer Metallkunde (1960) 51, 385-391

a=3.82Å b=3.82Å c=3.85Å

α=90° β=90° γ=90°

(Co0.8 Ru0.2)

Co_0.8Ru_0.2

Koester, W.Horn, E.

Zeitschrift fuer Metallkunde (1952) 43, 444-449

a=3.58Å b=3.58Å c=3.58Å

α=90° β=90° γ=90°

(Co0.8 Re0.2)

Co_0.8Re_0.2

Koester, W.Horn, E.

Zeitschrift fuer Metallkunde (1952) 43, 444-449

a=3.68Å b=3.68Å c=3.68Å

α=90° β=90° γ=90°

(Co0.8 Rh0.2)

Co_0.8Rh_0.2

Koester, W.Horn, E.

Zeitschrift fuer Metallkunde (1952) 43, 444-449

a=2.555Å b=2.555Å c=4.119Å

α=90° β=90° γ=120°